How to deal with the rust spots on the heating tube?

INDUSTRIAL HEATER    Heater Tube    How to deal with the rust spots on the heating tube?

The corrosion resistance of stainless steel heating tubes is not absolute, but relative and conditional. At present, there is no steel grade that does not corrode in any environment at home or abroad. Stainless steel electric heating tubes are also not applicable in any environment, so rust may occur. The long-term existence of rust spots not only affects the appearance, but also reduces the service life due to the surface corrosion of the stainless steel pipe. The rust spots on the surface of the stainless steel pipe should be treated in time. Today we will talk about how to deal with the rust spots on the heating tube?

 

Mechanical method:

 

Therefore, mechanically cleaned surfaces should be properly cleaned under dry conditions. The use of mechanical methods can only clean the surface, and cannot change the corrosion resistance of the material itself. Therefore, it is recommended to re-polishing with polishing equipment after mechanical cleaning and sealing with polishing wax.

 

Sandblasting, using glass or ceramic particle shot blasting, annihilation, brushing and polishing. It is possible to use mechanical methods to wipe off the pollution caused by the previously removed materials, polishing materials or annihilation materials. All kinds of pollution, especially foreign iron particles, can become a source of corrosion, especially in humid environments.

 

chemical method:

 

It is best to use a brush to wash several times during the treatment process. After the surface oxide scale is completely removed, rinse it with clean water (lime water or alkaline water is better) to avoid returning rust. After pickling, in order to remove all contaminants and acid residues, it is very important to rinse properly with clean water. After all treatments, re-polishing with polishing equipment and sealing with polishing wax. For those with slight rust spots, you can use a 1:1 gasoline and engine oil mixture to wipe off the rust spots with a clean cloth. Use spray or pickling paste to assist the re-passivation of the rusted parts to form a chromium oxide film to restore the corrosion resistance. Apply the pickling paste to the surface to be treated, the thickness of the coating film is 0.5-2mm, the general reaction time is 3-10 minutes or more, when it is used below 0°C or where the oxide scale is thick, the time needs to be extended appropriately.